WD1600 is chromium carbide composite cladding fusion bonded to a mild steel backing plate. The deposit has been realized by means of submerged arc welding. WD1600 wear plate is suitable for application involving high abrasion and medium to high impact.
Phone：+861807318303WD1600 is chromium carbide composite cladding fusion bonded to a mild steel backing plate. The deposit has been realized by means of submerged arc welding. WD1600 wear plate is suitable for application involving high abrasion and medium to high impact.
Impact resistant wear plates; Suited for applications involving high abrasion and medium to high impact.
|
Chemicals |
Hardness |
Sheet Size |
Base Metal |
|
C - Cr - Nb - Mo - Fe |
HRC 58-63 |
1400*3500/2100*3500 |
Q235/Q345. etc |
| Chemical Composition(%) |
C |
Cr |
Mn |
Si |
Mo+Nb+V |
Fe |
|
3.0-6.0 |
25.0-45.0 |
1.0-3.0 |
1.0-3.0 |
* |
Bal. |
|
| Hardness |
HRC 58-65 |
|||||
| Standard Thickness(mm) |
4+4; 5+5; 6+4; 6+6; 8+6; 8+8; 10+6; 10+8; 10+10; 12+12; 12+17; etc (overlay thickness up to 32mm) |
|||||
| Standard Sheet Size(mm) |
1400*3500; 2100*3500; (Customized size available) |
|||||
| ASTM G65 Procedure A |
0.09 - 0.16g |
|||||
| Operating Temperature |
<600 ℃ |
|||||
| Base Metal Material |
Q235B, Q345B; A36; S235JR and structural steels |
|||||
| Main Industry |
Mining, glass industry, cement plant, steel mill, power plant, etc |
|||||
| Fabrication |
Plasma cutting, Gouging, Countersunk, stud bolt, Bending |
|||||
Characteristics:
* Chromium carbide overlay wear resistant plate
* By submerged arc welding technology
* Chemical Composition: C: 3.0-6.0% Cr: 25-45%
* Chromium carbide Cr7C3 volume fraction about 50%
* The thickness of wear resistant layer can reach up to 50 mm
* Heat resistance up to 600°C
* Lager standard wear resistant area 1400*3000mm, 1400*3500mm, 2100*3500mm
* Better flatness with smooth surface
* Hardness: HRC58-65